Scientists in Iraq have applied an amorphous carbon nitride (CNx) thin film as an anti-reflective layer in commercial crystalline silicon solar cells. They claim they were able to improve their efficiency from 5.52 to 13.05%.

Researchers at the University of Technology-Iraq have developed a novel dual-function anti-reflection coating (ARC). They said it can significantly improve the power conversion efficiency of commercial crystalline silicon solar cells.

The coating is based on an amorphous carbon nitride (CNx) thin film that was synthesized by the radio frequency (RF) magnetron sputtering technique. The approach involves alternating the electrical potential of the current in a vacuum environment.

“This technique has an advantage over others in that it allows for precise control of deposition rate and thickness uniformity while using low-cost starting materials and producing no toxic byproducts,” the scientists explained. “We investigated the influence of deposition temperature and time on the properties of amorphous carbon nitride films deposited on glass and silicon substrates.”

They said that CNx films are suitable for applications in solar cells, due to their indirect bandgap, excellent mechanical strength, high thermal stability, low reflectivity, and high transmission. They investigate these properties and their impact on solar cell performance via field emission scanning electron microscope (FESEM) and an atomic force microscope (AFM). The films were deposited at different temperatures.

Their measurements showed that the films exhibited a high optical transmission in the range of 200 nm to 2500 nm. Films deposited at a lower temperature are much more transparent than films deposited at a higher temperature.

“The transmission of the film prepared at room temperature was 91% at 550 nm. Whereas the optical transmission of the film prepared at 200 C decreased to 81% at 550 nm. The films have a transmission of between 52% to 96% in the visible region (350 nm to 780 nm) and higher than 89% in the near-infra-red (NIR) region,” the group said, noting that the increase in Nitrogen content in the film structure results in an increase in the optical energy gap.

The film was then deposited over commercial c-Si solar cells at a deposition time and temperature of 120 minutes and 200 C, respectively, and the performance of the solar devices was measured under standard illumination conditions. Their short circuit current increased from 14.69 to 33.85 mAcm−2 and the efficiency climbed from 5.52% to 13.05%.

“In principle, the effect of the short-circuit current reflects the actual of the ARC, since it is directly related to the reduction of the surface reflectance and hence increases the photocurrent generated by the efficiency photons absorbed in the solar cell,” they said , noting that the open-circuit voltage increased slightly and that its fill factor was almost equal to that of the uncoated cell.

“This study shows that CNx films have promising application potential as an efficient ARC for c-Si solar cells as compared to traditional ARC materials,” the academics concluded, without providing details on the costs of the proposed technology. They introduced the novel coating technology in “Amorphous carbon nitride dual-function anti-reflection coating for crystalline silicon solar cells,” which was recently published in Scientific Reports.